Dongbaek Fine - Chem
제품안내
- HOME
- >
- 제품안내
- >
- PI Film
PI Film
DFPI-101F , DFTPI-201F , DFCPI-301F 코팅 필름은 넓은 온도 범위에서 뛰어난 기계적 성능 및 전기적 특성을 증명
하였습니다.
적용분야
– Flexible Display 및 산업전반 활용
DFPI-101F 열경화성 PI 필름
Item | Units | Specification | Typical Result | |
---|---|---|---|---|
Thickness | Um | 23.0 ~ 27.0 | 25.0 | |
Ultimate Tensile strength | MD | MPa | > 170 | 220 |
TD | MPa | > 160 | 180 | |
Ultimate Elongation | MD | % | > 50 | 60 |
TD | % | > 50 | 80 | |
Young's modulus | MD | MPa | > 2500 | 3000 |
TD | MPa | > 2000 | 2500 | |
Surface tension | Belt Side | Dynes'cm | > 58 | 64 |
Air Side | Dynes'cm | > 58 | 64 | |
Dielectric strength | KV / mm | > 200 | 255 |
DFTPI-201F 열가소성 PI 필름
1. Termal Properties
특성 | 단위 | DFTPI-201F필름 | 비고 |
---|---|---|---|
Tg | ºC | >280 | DSC |
CTE | ppm | < 30 | TMA |
Td | ºC | > 500 | TGA |
2. Mechanical Properties
특성 | 단위 | DFTPI-201F필름 | 비고 |
---|---|---|---|
Peel Strength | kgf/cm | > 1.0 | ASTM 882 |
Water Absorption | % | > 2.0 | – |
Solder Resistance | - | Pass | 300ºC/1min |
DFCPI-301F PI 투명 필름
특성 | 조건 | 15㎛ | 25㎛ | 측정방법 | |
---|---|---|---|---|---|
기계적 특성 | 인장강도 | 150MPa | 150MPa | JIS K7161 | |
탄성율 | 3.5Gpa | 3.5Gpa | JIS K7161 | ||
전연신 | 8% | 8% | JIS K7161 | ||
열적 특성 | 유리전이온도 | 300ºC | 300ºC | DMA | |
선열창계수 | 50~150ºC | 45 ppm / ºC | 45 ppm / ºC | TMA | |
가열치수변화 | 200ºC x 30min | -0.14% | -0.14% | JIS K7133 | |
광학 특성 | 투멍률 | 88% | 88% | JIS K7105 | |
광투과율 | @380nm | 0.6% | 0% | JIS K0115 | |
@400nm | 54% | 40% | |||
@550nm | 87% | 87% | |||
전기 특성 | 전열파괴강도 | AC | 180 kV / mm | 180 kV / mm | JIS K6911 |
체적저항율 | DC100v | > 1014 Ω cm | > 1014 Ω cm | JIS K6911 | |
표면저항율 | DC100v | > 1014 Ω | > 1014 Ω | JIS K6911 | |
그밖의 특성 | 흡수율 | 1.60% | 1.60% | JIS K7209 | |
굴절율 | 589nm | 1.68 | 1.68 | JIS K7142 |
폴리페닐렌 설파이드(PPS) 필름
Property | unit | 9-3030 | 12-3030 | 16-3030 | 25-3030 | Testing method | |
---|---|---|---|---|---|---|---|
Thickness | MMV | ㎛ | 9.36 | 12.4 | 16.3 | 25.1 | JIS C 2151 |
Tensile strength | MD | MPa | 249 | 233 | 240 | 268 | JIS C 2151 |
TD | 227 | 229 | 243 | 230 | |||
Elongation | MD | % | 82 | 80 | 86 | 80 | JIS C 2151 |
TD | 94 | 94 | 89 | 98 | |||
Tear strength | MD | N / 20mm | 58 | 77 | 110 | 171 | JIS C 2151 |
TD | 64 | 80 | 111 | 186 | |||
Heat shrinkage (150℃ - 30min) |
MD | % | 1.4 | 1.5 | 1.5 | 1.7 | JIS C 2151 or ASTM D 1204 |
TD | 0.1 | -0.3 | 0.0 | -0.3 | |||
Heat shrinkage (230℃ - 10min) |
MD | % | 4.4 | - | - | - | JIS C 2151 or ASTM D 1204 |
TD | 0.3 | - | - | - | |||
Heat shrinkage (250℃ - 10min) |
MD | % | - | 6.4 | 7.0 | 8.1 | JIS C 2151 ASTM D 1204 |
TD | - | 1.3 | 3.3 | 3.1 | |||
Surface wet tension | corona treatment side | mN/m | 72 | 72 | 72 | 72 | JIS K 6768 |
Breakdown voltage (AC,sheet) |
Ave | kV | 1.8 | 2.5 | 3.2 | 6.0 | JIS C 2151 |
Volume resistivity | Ave | Ω cm | 3.6 x 1017 | 4.6 x 1017 | 2.6 x 1017 | 2.3 x 1017 | JIS C 2151 |
Property | unit | 38-3030 | 50-3030 | 75-3030 | 100-3A30 | Testing method | |
---|---|---|---|---|---|---|---|
Thickness | MMV | ㎛ | 38.1 | 50.1 | 75.1 | 99.3 | JIS C 2151 |
Tensile strength | MD | MPa | 271 | 300 | 292 | 271 | JIS C 2151 |
TD | 224 | 213 | 204 | 195 | |||
Elongation | MD | % | 81 | 71 | 72 | 73 | JIS C 2151 |
TD | 102 | 108 | 108 | 112 | |||
Tear strength | MD | N / 20mm | 262 | 340 | 491 | 622 | JIS C 2151 |
TD | 286 | 379 | 539 | 674 | |||
Heat shrinkage (150℃ - 30min) |
MD | % | 1.5 | 1.7 | 1.4 | 1.2 | JIS C 2151 or ASTM D 1204 |
TD | -0.2 | -0.1 | 0.0 | -0.2 | |||
Heat shrinkage (230℃ - 10min) |
MD | % | - | - | - | - | JIS C 2151 or ASTM D 1204 |
TD | - | - | - | - | |||
Heat shrinkage (250℃ - 10min) |
MD | % | 7.6 | 8.5 | 8.1 | 6.7 | JIS C 2151 ASTM D 1204 |
TD | 3.0 | 4.5 | 4.5 | 3.1 | |||
Surface wet tension | corona treatment side | mN/m | 72 | 72 | 72 | 72 | JIS K 6768 |
Breakdown voltage (AC,sheet) |
Ave | kV | 9.2 | 11.0 | 14.1 | 17.2 | JIS C 2151 |
Volume resistivity | Ave | Ω cm | 3.1 x 1017 | 2.4 x 1017 | - | - | JIS C 2151 |
DF PET 필름
Item | Units | Test Method | Typical Result | |
---|---|---|---|---|
Thickness | ㎛ | Method | 50 | |
Tensile Strength | MD | kg / ㎡ | ASTM D882 | 23.6 |
TD | 18.6 | |||
Elongation | MD | % | 143 | |
TD | 131 | |||
Heat Shrinkage | MD | % | ASTM D1024 (190℃,20min) |
1.6 |
TD | 0.0 | |||
Surface Tension | IN | dyne / cm | ASTM D2578 | 56 |
OUT | - | |||
Haze | % | ASTM D1003 | 2.5 | |
Surface Tension | O / O | - | ASTM D1894 | 0.35 |
I / I | 0.37 |
TLT 필름 / PICF 필름
PPS + PET 필름 - TLT Film
TLT 필름은 PET 필름 양면에 PPS 필름을 합지한 제품입니다.
장점은 PPS 필름에 비해 가격이 저렴합니다.
PI + PET 필름 - PICF Film
PICF 필름은 PET 필름 양면에 PI 용액을 코팅한 필름입니다.
장점은 PI 필름에 비해 가격이 저렴하며, 내습성과 인쇄성이 뛰어납니다.